Dx53d Z140
DX53D Z140 galvanized steel is a high-formability steel with a thicker zinc coating that provides improved corrosion resistance.
Its key characteristics include:
- Excellent deep drawing and stamping performance
- Strong corrosion protection due to Z140 coating
- Stable mechanical properties
- Suitable for complex formed industrial components
- Sự miêu tả
Sự miêu tả
DX53D Z140 is a hot-dip galvanized steel grade with excellent deep-drawing performance and a relatively heavy zinc coating of 140 g/m -mét (Z140 coating class). It is widely used in applications that require strong formability combined with enhanced corrosion resistance, especially in automotive, sự thi công, và sản xuất thiết bị.
This material combines a low-carbon steel substrate with a thicker zinc coating, providing longer service life in moderately corrosive environments.
1. What Is DX53D Z140?
Thép mạ kẽm DX53D is a cold-rolled, deep-drawing quality steel designed for complex forming operations.
- DX53D → deep drawing steel grade with high ductility
- Z140 → zinc coating mass approximately 140 g/m -mét
- Standard system → EN 10346 thép mạ kẽm nhúng nóng
Compared with Z100, Z140 provides better corrosion protection due to a thicker zinc layer.
2. Chemical Composition of DX53D Base Steel
The steel substrate is optimized for high formability:
| Yếu tố | Nội dung (%) | Chức năng |
|---|---|---|
| Cacbon (C) | 0,10–0,12 | Maintains ductility |
| Mangan (Mn) | ≤ 0.60 | Cải thiện độ dẻo dai |
| Silicon (Và) | ≤ 0.50 | Controls steel structure |
| Phốt pho (P) | ≤ 0.10 | Impurity control |
| lưu huỳnh (S) | ≤ 0.045 | Cải thiện kiểm soát khả năng gia công |
| Nhôm (Al) | ≥ 0.015 | Khử oxy và tinh chế hạt |
| Nitơ (N) | ≤ 0.012 | Ổn định cấu trúc |
👉 Thành phần này đảm bảo excellent elongation and deep drawing capability.
3. Thành phần mạ kẽm (Z140 Layer)
The Z140 coating is applied by hot-dip galvanizing:
| Thành phần | Sự miêu tả |
|---|---|
| kẽm (Zn) | Lớp bảo vệ chính |
| Iron-Zinc alloy layer | Bonding interface |
| Khối lượng phủ | ~140 g/m² total |
👉 The thicker coating compared to Z100 significantly improves corrosion resistance and service life.
4. Mechanical Properties of DX53D Z140
Thép mạ kẽm DX53D offers excellent forming performance:
| Tài sản | Giá trị |
|---|---|
| Độ bền kéo | 270 – 380 MPA |
| Sức mạnh năng suất | 140 – 260 MPA |
| Độ giãn dài | ≥ 28 – 40% |
| độ cứng | ~80 – 120 HB |
| Mô đun đàn hồi | ~210 GPa |
👉 Tính năng chính: very high elongation for complex stamping and deep drawing.
5. Functional Properties
- Hiệu suất vẽ sâu tuyệt vời
- Strong corrosion resistance (better than Z100)
- Chất lượng bề mặt tốt để sơn hoặc phủ
- Stable performance in stamping and bending
- Khả năng hàn tốt (spot and arc welding)
6. Role of Z140 Zinc Coating
The Z140 coating provides enhanced protection:
Chống ăn mòn
- Thicker zinc layer extends service life
- Better performance in humid or outdoor environments
- Sacrificial protection against rust
Bảo vệ bề mặt
- Protects steel from oxygen and moisture
- Maintains durability during storage and transport
Industrial Stability
- Suitable for long-term use in exposed conditions
7. Common Applications of DX53D Z140
Thép mạ kẽm DX53D được sử dụng rộng rãi trong:
- Automotive body panels and structural parts
- Home appliance housings (máy giặt, refrigerators)
- Electrical cabinets and enclosures
- Hệ thống ống dẫn HVAC
- Light steel framing components
- Bộ phận đóng dấu công nghiệp
- Construction accessories and panels
8. DX53D Z140 vs Z100 Comparison
| Tài sản | Z100 | Z140 |
|---|---|---|
| Zinc coating weight | 100 g/m -mét | 140 g/m -mét |
| Chống ăn mòn | Tốt | Tốt hơn |
| Service life | Trung bình | Longer |
| Cost level | Thấp hơn | Slightly higher |
| Môi trường ứng dụng | trong nhà / ngoài trời nhẹ nhàng | ngoài trời / môi trường ẩm ướt |